High strength geocell

Word:[Big][Middle][Small] QR Code 2023/4/28     Viewed:    


Product performance

  The sheet material of high-strength geotextile cell is made of linear polypropylene (PP) after high-temperature heating and extrusion, and then stretched. The attachment rivets and riveting joints of the cell are made of steel three hole 1mm thick galvanized steel sheet and modified PET sheet, which are riveted with a core pulling riveting gun.


Applicable scope

  Soft foundation treatment of expressways, first-class highway, railways, municipal roads, airport roads and ports can also be used to control landslides, build retaining walls, bridge abutment jumping and landscaping.


Technical parameter


Reference standard JT/T516-2004


Serial Number

project

unit

technical requirement

1

Cell height

cm+0.2

5-20

2

Tensile breaking strength of cell sheets (longitudinal)

KN/5cm

3.5

3

Ultimate peel strength at riveting point

KN/m

2.7

4

mesh size

cm+2

40×40/25×25

5

elongation at break

%

13




Reference standard Q/AHZW01-2007

Dimensional deviation

Model

Cell height

H/mm

Cell thickness(T/mm

Cell welding distance

A/mm

 

Nominal value

deviation

Nominal value

Nominal value

deviation

1

H100

+5

0.5

300A800

+15

2

H100200

+5.5

Mechanical indicators

Serial Number

Test items

unit

Material PP compartment

Material PP compartment

1

appearance

 

The cells are flat, without bubbles or grooves

2

Longitudinal tensile yield strength of cells

Mpa

150-200

150-200

3

Tensile strength at the rivet

N/cm

100

100

4

Longitudinal Elongation of Cells

%

15

15